高频磁场下原位合成Al3(Ti0.5Zr0.5)p/6005A复合材料的显微组织与性能
Microstructure and Properties of In-Situ Synthesized Al3(Ti0.5Zr0.5)p/6005A Composites under High-frequency Magnetic Field
以K2TiF6、K2ZrF6与Na3AlF6为反应物, 在高频磁场下, 采用熔体反应法原位合成了 Al3(Ti0.5Zr0.5)p/6005A复合材料; 通过扫描电镜、X射线衍射仪、拉伸试验机等对复合材料的组织与性能进行了研究。结果表明: 磁场下原位生成了细小的Al3(Ti0.5Zr0.5)颗粒, 平均尺寸为1~3 μm, 且弥散分布于基体中; 在磁场频率为2 MHz时复合材料的屈服强度、抗拉强度分别为279?4, 305.8 MPa, 较基体的提高了7.1%和8.7%, 伸长率为9.5%, 较基体的下降了10.1%; 复合材料的断裂特征由基体的韧性断裂转变为混合型断裂。标&&&&签
Al3(Ti0.5Zr0.5)p/6005A composites were in-situ synthesized under high-frequency magnetic field by direct melt reaction using K2TiF6, K2ZrF6 and Na3AlF6 as reactants. By means of scanning electron microscopy, X-ray diffraction and tensile testing machine, the microstructure and properties of the composites were investigated. The results show that the in-situ synthesized particles under magnetic field were fine Al3(Ti0.5Zr0.5)p particles, whose average size was 1-3 μm and dispersively distributed in Al substrate. At magnetic frequency of 2 MHz, the yield strength, tensile strength of the composites were 279.4 and 305.8 MPa, which increased by 7.1% and 8.7% compared with that of the substrate. And the elongation was 9.5%, which decreased by 10.1%. The fracture characteristics of the composites transformed from ductile fracture of the substrate to mixing fracture.
中图分类号
国家“863”高技术研究项目(); 江苏省六大人才高峰项目(06-D-021); 江苏大学高级专业人才科研启动基金资助项目(07JDG084); 教育部科学技术研究重点项目(207038)
修改稿日期
网络出版日期
作者单位点击查看备注祝晓辉(1984-), 男, 江西上饶人, 硕士研究生。
引用该论文:
ZHU Xiao-hui,ZHAO Yu-tao,LI Gui-rong,CHEN Gang,SHE Chang-jun,XUAN Dong-hua,ZHENG Meng.&Microstructure and Properties of In-Situ Synthesized Al3(Ti0.5Zr0.5)p/6005A Composites under High-frequency Magnetic Field[J].&Materials for mechancial engineering,&):&71～75祝晓辉,赵玉涛,李桂荣,陈刚,佘昌俊,轩动华,郑梦.&高频磁场下原位合成Al3(Ti0.5Zr0.5)p/6005A复合材料的显微组织与性能[J].&机械工程材料,&):&71～75
共有人对该论文发表了看法，其中：
人认为该论文很差
人认为该论文较差
人认为该论文一般
人认为该论文较好
人认为该论文很好
参考文献【1】ZHAO Y T, DAI Q X, CHENG X N,et al. Microstructure characterization of reinforcements in in-situ synthesized composites of the system Al-Zr-O[J].Transactions of Nonferrous Metals Society of China,):108-112.&【2】许可,赵玉涛,陈刚,等.Sr对( Al2O3+Al3Zr)p/A356复合材料组织及性能的影响[J].特种铸造及有色合金,):139-141.&【3】张发云,闫洪,周天瑞,等.金属基复合材料制备工艺的研究进展[J].锻压技术,0-105.&【4】严学华,孙少纯,蒋宗宇.原位反应复合材料研究进展[J].铸造设备研究,-30.&【5】张高科,陈虹.材料制备及加工中的磁化学研究及应用[J].硅酸盐通报,-37.&【6】&【7】KARPETS M V, MILMAN Y V, BARABSH O M,et al. The influence of Zr alloying on the structure and properties of Al3Ti[J].Intermetallics,-249.&【8】AIKIN JR R M, CHRISTODUCLOU L. Script metal[J].Et Mater,-14.&【9】MASSALSKI T B.ASM binary alloy phase diagrams[M].OH: ASM International,2004.&【10】乐永康,张建平,陈东.原位反应合成TiB2的生长行为[J].特种铸造及有色合金,):102-105.&【11】李桂荣.原位制备颗粒增强铝基复合材料的组织控制和性能研究[D].镇江:江苏大学,.&
如果您尚未在本站注册，请点击此处【】
往期精选文章
www. Copyright (C),All Rights Reserved 版权所有&&声明：本站内容部分源于网络转载，出于传递更多信息之目的，并不意味着赞同其观点或证实其描述。文章内容仅供参考，请咨询相关专业人士。
如果无意之中侵犯了您的版权，或有意见、反馈或投诉等情况, 请联系本站，
Copyright (C)
| 欢迎来到杭州厨师培训您的位置：
磁场诱导下原位制备CS-Fe3O4杂化膜及其渗透蒸发性能的研究
磁场诱导下原位制备CS-Fe3O4杂化膜及其渗透蒸发性能的研究
Fabrication of hybrid membranes for ethanol dehydration by the magnetic alignment of in situ-generated Fe3O4 nanoparticles within chitosan matrix
发布时间：　　浏览量：0　　收藏数：0　　评论数：
天津大学化工学院，天津
高分子-无机杂化膜可以综合高分子材料和无机材料的优点，受到国内外学者广泛的关注。无机材料在杂化膜内的分布是影响膜性能的重要因素之一。本研究通过磁场诱导调控壳聚糖膜内原位生成的Fe3O4纳米颗粒的空间分布，并通过扫描电镜（SEM）、透射电镜（TEM）、x射线衍射（XRD）等对膜的结构和分离性能进行表征。结果表明，原位生成的Fe3O4沿着磁场线方向成串排列，并且垂直于膜表面。杂化膜用于渗透蒸发乙醇脱水过程，磁场诱导下的杂化膜性能有所提高，最佳性能为渗透通量1042 g/m2h，分离因子674（透过液水含量98.3%）。
膜分离；杂化膜；磁场诱导；原位；Fe3O4颗粒；渗透蒸发
Xing Ruisi，
ZHAO Cuihong，
PAN Fusheng*
School of Chemical Engineering and Technology, Tianjin University, Tianjin
Abstract：
The polymer-inorganic hybrid membranes can combine the advantages of polymer and inorganic materials, which have been widely concerned. The distribution of inorganic materials in the hybrid membranes is one of the key factors that determining their performance. Chitosan-Fe3O4 hybrid membranes were fabricated by combining in situ method and magnetic alignment approach was used to adjust the distribution of Fe3O4 nanoparticles. Scanning electron microscopy (SEM), transmission electron microscopy (TEM) and X-ray diffractometer (XRD) were utilized to characterize the structure of the hybrid membranes. The results showed that the Fe3O4 nanoparticles were aligned into chain-like bunches. The fabricated chitosan-Fe3O4 hybrid membranes exhibited an enhanced permeability for the pervaporation of water/ethanol mixture. Under optimum conditions, the hybrid membrane permeation flux reached 1042 g/m2h, and a separation factor of 674 with concentration of water in permeate solution of 98.3 wt.%.
Keywords：
Membrane S H Magnetic- Fe3O4 Pervaporation
PDF全文下载：
作者简介：
邢瑞思（1991-），女，硕士生，膜分离
通信联系人：
潘福生（1982-），男，副研究员，膜分离
【收录情况】
中国科技论文在线：邢瑞思，赵翠红，潘福生.&磁场诱导下原位制备CS-Fe3O4杂化膜及其渗透蒸发性能的研究[EB/OL].北京：中国科技论文在线&
[].http://www./releasepaper/content/.
发表期刊：
首发论文搜索
&> 信息科学与系统科学
&> 地球科学
&> 畜牧、兽医科学
&> 基础医学
&> 临床医学
&> 预防医学与卫生学
&> 军事医学与特种医学
&> 中医学与中药学
&> 工程与技术科学基础学科
&> 测绘科学技术
&> 材料科学
&> 矿山工程技术
&> 冶金工程技术
&> 机械工程
&> 动力与电气工程
&> 能源科学技术
&> 核科学技术
&> 电子、通信与自动控制技术
&> 计算机科学技术
&> 化学工程
&> 纺织科学技术
&> 食品科学技术
&> 土木建筑工程
&> 水利工程
&> 交通运输工程
&> 航空航天科学技术
&> 环境科学技术
&> 安全科学技术
&> 图书馆、情报与文献学
&> 体育科学
尊敬的作者，欢迎您在本站投稿：
注：请投稿作者直接在本站注册并登录提交文章，
任何个人或机构宣称代理在本站投稿均为侵权行为
本学科今日推荐
本文作者合作关系
本文相关论文
化学工程其他学科催化反应工程萃取化学分离工程化工传递过程
&&&&&&&&&&&&&&
中国科技论文在线
&|&&|&&|&&|&&|&nbsp
化学工程基础学科
化工测量技术与仪器仪表
化工传递过程
化学分离工程
化学反应工程
化工系统工程
化工机械与设备
无机化学工程
有机化学工程
电化学工程
高聚物工程
煤化学工程
石油化学工程
精细化学工程
毛皮与制革工程
生物化学工程
化学工程其他学科
磁场诱导下原位制备CS-Fe3O4杂化膜及其渗透蒸发性能的研究
&&收藏本文
&&推荐本文给好友
&&订阅本文所在学科
&&分享到我的圈子
多个邮箱请用逗号“，”隔开
分享到我的圈子感应电磁场对原位形成尖晶石与显微结构的影响--《第十八届全国高技术陶瓷学术年会摘要集》2014年
感应电磁场对原位形成尖晶石与显微结构的影响
【摘要】：正感应加热是利用感应线圈中的交变电磁场在工件中产生涡流发热来达到加热工件的目的,具有快速、清洁、节能、易于实现自动化和生产效率高等特点。铝镁尖晶石质耐火材料被广泛应用于各类感应炉的炉衬,在其基质内部常常存在着尖晶石化的反应。但是感应电磁场对尖晶石的原位生成和烧结的影响至今未见报道。本文以活性氧化铝粉和高纯电熔镁砂为原料在中频感应炉中烧结形成尖晶石。通过XRD、SEM等检测手段分析了感应炉的功率、加热时间及不同Al_2O_3/MgO比对尖晶石的形成和烧结的影响。结果表明:
【作者单位】：
【分类号】：TQ175.1【正文快照】：
感应加热是利用感应线圏中的交变电磁场在工件中产生涡流发热来达到加热工件的目的,具有快速、清洁、节能、易于实现自动化和生产效率高等特点。铝镁尖晶石质耐火材料被广泛应用于各类感应炉的炉衬,在其基质内部常常存在着尖晶石化的反应^但是感应电磁场对尖晶石的原位生成和
欢迎：、、)
支持CAJ、PDF文件格式，仅支持PDF格式
&快捷付款方式
&订购知网充值卡
400-819-9993
《中国学术期刊（光盘版）》电子杂志社有限公司
同方知网数字出版技术股份有限公司
地址：北京清华大学 84-48信箱 大众知识服务
出版物经营许可证 新出发京批字第直0595号
订购热线：400-819-82499
服务热线：010--
在线咨询：
传真：010-
京公网安备75号基于取向结构的仿生各向异性纳米复合水凝胶--《中国化学会第30届学术年会摘要集-论坛二：新型前沿交叉化学论坛》2016年
基于取向结构的仿生各向异性纳米复合水凝胶
【摘要】：高分子水凝胶由于其与生物软组织结构和性能类似的"湿和软"的特性,使其成为最为理想的生物医用材料。但是与生物软组织相比,传统的高分子水凝胶力学性能较差并且结构上各向同性,从而限制其进一步应用。我们采用高分子与无机半导体纳米片复合的方法制备水凝胶材料。发现氧化钛纳米片可以利用水作为自由基的来源,起到光引发剂的作用,同时在结构上可以通过与高分子间的非共价作用形成交联网络,从而增强凝胶的力学性能[1]。进而我们发现胶体分散的单层氧化钛纳米片在磁场中可以垂直于磁感线方向取向,并形成长程有序的周期性结构,通过原位的高分子聚合,可以获得力学性能、光学性能及驱动性能各向异性的水凝胶材料[2,3]。由于纳米片间的静电排斥力可以抵抗外界施加在垂直于纳米片平面方向上的压力,从而在一维方向上增强凝胶的弹性模量。以上研究对于理解生命体中带电生物大分子的组装行为,仿生制备多级有序结构的生物组织材料具有重要的意义。
【作者单位】：
【关键词】：
【分类号】：TQ427.26;R318.08【正文快照】：
基于取向结构的仿生各向异性纳米复合水凝胶@刘明杰$北京航空航天大学化学与环境学院!北京100190高分子水凝胶由于其与生物软组织结构和性能类似的"湿和软"的特性,使其成为最为理想的生物医用材料。但是与生物软组织相比,传统的高分子水凝胶力学性能较差并且结构上各向同性,从
欢迎：、、)
支持CAJ、PDF文件格式，仅支持PDF格式
【相似文献】
中国期刊全文数据库
杨智韬;高军;瞿金平;;[J];中国塑料;2009年01期
聂辉泉;常凤眉;赵汉强;林伟生;梁佩源;余爱芳;;[J];广州化学;1988年01期
吴丝竹,李荣彬,吴刚;[J];高分子材料科学与工程;2000年02期
陈前军;[J];广东化纤;1998年01期
赵平;王朝余;傅强;;[J];塑料工业;2007年S1期
安娜;徐樑华;张峰;吴丝竹;;[J];高分子材料科学与工程;2008年01期
;[J];;年期
中国重要会议论文全文数据库
徐强;曹维宇;徐梁华;吴丝竹;;[A];2004年全国高分子材料科学与工程研讨会论文集[C];2004年
王彬;张海龙;肖士洁;高爱君;徐樑华;;[A];复合材料：创新与可持续发展(上册)[C];2010年
王彬;张海龙;肖士洁;高爱君;徐樑华;;[A];复合材料：创新与可持续发展(上册)[C];2010年
张峰;安娜;徐樑华;吴丝竹;;[A];复合材料——基础、创新、高效：第十四届全国复合材料学术会议论文集（上）[C];2006年
曹维宇;温光和;徐樑华;;[A];复合材料：创新与可持续发展(上册)[C];2010年
曹维宇;温光和;徐樑华;;[A];复合材料：创新与可持续发展(上册)[C];2010年
中国博士学位论文全文数据库
王彬;[D];北京化工大学;2012年
中国硕士学位论文全文数据库
李龙;[D];北京化工大学;2014年
&快捷付款方式
&订购知网充值卡
400-819-9993
《中国学术期刊（光盘版）》电子杂志社有限公司
同方知网数字出版技术股份有限公司
地址：北京清华大学 84-48信箱 大众知识服务
出版物经营许可证 新出发京批字第直0595号
订购热线：400-819-82499
服务热线：010--
在线咨询：
传真：010-
京公网安备75号}